Artikel: Fe-Based Amorphous Magnetic Powder Cores with Low Core Loss Fabricated by Novel Gas-Water Combined Atomization Powders.
Materials (Basel, Switzerland)
2022 Band 15, Heft 18
Abstract: FeSiBCCr amorphous powders were produced by a novel gas-water combined atomization process, and the corresponding MPCs (magnetic powder cores) were subsequently fabricated by phosphating treatment (0.4~1.6 wt.%), cold pressing (550~2350 MPa), and ... ...
Abstract | FeSiBCCr amorphous powders were produced by a novel gas-water combined atomization process, and the corresponding MPCs (magnetic powder cores) were subsequently fabricated by phosphating treatment (0.4~1.6 wt.%), cold pressing (550~2350 MPa), and annealing (423~773 K), respectively. The results showed that the powders had high circularity, excellent thermal stability (ΔT = 59 K), and high saturation magnetization (0.83 T), which could provide raw powders for high-performance MPCs. With increasing phosphoric acid concentrations, despite the increase in DC-bias%, the uniformity of the insulation layers deteriorated, which led to a decrease in permeability and an increase in core loss. With increasing compaction pressures, the core loss increased continuously, and the permeability and DC-bias% first increased and then decreased. When annealing below the crystallization temperature, with increasing annealing temperatures, the permeability increased, and the core loss and DC-bias% decreased continuously. Under the optimized process of 0.4 wt.% phosphating concentration, 550 MPa pressure, and 773 K annealing temperature, the MPCs had a permeability of 21.54 ± 1.21, DC-bias% of 90.3 ± 0.2, and a core loss ( |
---|---|
Sprache | Englisch |
Erscheinungsdatum | 2022-09-10 |
Erscheinungsland | Switzerland |
Dokumenttyp | Journal Article |
ZDB-ID | 2487261-1 |
ISSN | 1996-1944 |
ISSN | 1996-1944 |
DOI | 10.3390/ma15186296 |
Datenquelle | MEDical Literature Analysis and Retrieval System OnLINE |