Artikel: Defect Chemistry of Titanium Dioxide: Evidence of the n-p Transition during Cooling
Journal of physical chemistry. 2022 Mar. 07, v. 126, no. 10
2022
Abstract: This work reports on the semiconducting properties of TiO₂ (rutile) during cooling from 1273 K to room temperature in the gas phase of controlled oxygen activity. The studies are based on simultaneous in situ monitoring of electrical conductivity and ... ...
Abstract | This work reports on the semiconducting properties of TiO₂ (rutile) during cooling from 1273 K to room temperature in the gas phase of controlled oxygen activity. The studies are based on simultaneous in situ monitoring of electrical conductivity and thermoelectric power. The changes in semiconducting properties during cooling are preferentially related to surface properties, and they depend on oxygen activity during prior annealing and the cooling procedure. We show that annealing in strongly oxidizing conditions, at p(O₂) = 100 kPa, results in the imposition of p-type properties, and cooling results in an enhancement of p-type properties. However, annealing at 1273 K in mildly oxidizing conditions, at p(O₂) = 10 Pa, results in the imposition of n-type properties and subsequent cooling results in the n-p transition at 950 K. The observed surprising shift toward p-type properties during cooling is considered in terms of preferential ionization of the predominant acceptor-type ionic defects, titanium vacancies. TiO₂ reduced in the argon–hydrogen mixture exhibits n-type semiconducting properties during annealing at 1273 K and subsequent cooling. The latter n-type behavior is induced by decreased oxygen activity leading to the formation of intrinsic donor-type ionic defects (oxygen vacancies and titanium interstitials) and the formation of donor-type hydrogen-related extrinsic defects. |
---|---|
Schlagwörter | ambient temperature ; cooling ; electrical conductivity ; ionization ; oxygen ; physical chemistry ; semiconductors ; titanium ; titanium dioxide |
Sprache | Englisch |
Erscheinungsverlauf | 2022-0307 |
Umfang | p. 5014-5021. |
Erscheinungsort | American Chemical Society |
Dokumenttyp | Artikel |
ISSN | 1932-7455 |
DOI | 10.1021/acs.jpcc.1c09938 |
Datenquelle | NAL Katalog (AGRICOLA) |
Zusatzmaterialien
Kategorien
Über subito bestellen
Dieser Service ist kostenpflichtig (siehe Lieferbedingungen von subito). Bestellungen, die einen Artikel nebst Supplementary Material umfassen, werden grundsätzlich wie mehrfache Bestellungen bearbeitet. Gebühren fallen in diesen Fällen für jede einzelne Bestellung an.
Fernleihe an ZB MED
Sie können sich den gewünschten Titel als lokale Nutzerin oder lokaler Nutzer von ZB MED direkt an den Standort Köln schicken lassen.